Manufacturer: INEOS
Produced At: Korea / China
Product Category: ABS
Product No: Terluran GP-22
Product Quantity: 25KG / BAG
Product Features: Good Colorability,Good Impact Resistance,Good Surface Finish,High Gloss,Medium Flow
Terluran? GP-22
Excellent colorability
Medium flow
Good impact resistance
Good heat distortion resistance
High quality surface finish and gloss
Injection molding
Appliance housings
Household and sanitary appliances
Toys
Automotive components
Features |
|
Uses |
|
Forms |
|
Processing Method |
|
Multi-Point Data |
|
Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | |||
-- | 1.04 | ASTM D792 | |
-- | 1.04 | g/cm? | ISO 1183 |
Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
200°C/5.0 kg | 1.5 | g/10 min | |
220°C/10.0 kg | 19 | g/10 min | |
Melt Volume-Flow Rate (MVR) | |||
230°C/3.8 kg | 0.293 | in?/10min | ASTM D1238 |
220°C/10.0 kg | 1.16 | in?/10min | ISO 1133 |
Molding Shrinkage | |||
Flow | 4.0E-3 to 7.0E-3 | in/in | ASTM D955 |
-- | 0.40 to 0.70 | % | ISO 294-4 |
Water Absorption | |||
Saturation, 73°F | 1.0 | % | ASTM D570, ISO 62 |
Equilibrium, 73°F, 50% RH | 0.22 | % | ISO 62 |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 103 | ASTM D785 | |
Ball Indentation Hardness | 14100 | psi | ISO 2039-1 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 334000 | psi | ASTM D638, ISO 527-2 |
Tensile Strength | |||
Yield, 73°F | 6520 | psi | ASTM D638 |
Yield, 73°F | 6530 | psi | ISO 527-2 |
Tensile Strain | |||
Yield, 73°F | 2.6 | % | ISO 527-2 |
Break | 2.6 | % | ASTM D638 |
Nominal Tensile Strain at Break (73°F) | 10 | % | ISO 527-2 |
Flexural Modulus | 334000 | psi | ASTM D790 |
Flexural Strength | 9430 | psi | ASTM D790, ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | ||
-22°F | 3.8 | ft·lb/in? | |
73°F | 10 | ft·lb/in? | |
Charpy Unnotched Impact Strength | ISO 179 | ||
-22°F | 48 | ft·lb/in? | |
73°F | 86 | ft·lb/in? | |
Notched Izod Impact | |||
-22°F | 1.1 | ft·lb/in | ASTM D256 |
0°F | 1.9 | ft·lb/in | ASTM D256 |
73°F | 5.6 | ft·lb/in | ASTM D256 |
-22°F | 3.8 | ft·lb/in? | ISO 180/A |
73°F | 12 | ft·lb/in? | ISO 180/A |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
66 psi, Unannealed | 195 | °F | ASTM D648 |
66 psi, Annealed | 219 | °F | ASTM D648 |
66 psi, Annealed 2 | 210 | °F | ISO 75-2/B |
264 psi, Unannealed | 172 | °F | ASTM D648 |
264 psi, Annealed | 210 | °F | ASTM D648 |
264 psi, Annealed 2 | 201 | °F | ISO 75-2/A |
Vicat Softening Temperature | |||
-- | 221 | °F | ISO 306/A50 |
-- | 205 | °F | ISO 306/B50 |
CLTE - Flow | 4.4E-5 to 6.1E-5 | in/in/°F | ISO 11359-2 |
Thermal Conductivity | 1.2 | Btu·in/hr/ft?/°F | DIN 52612 |